Metakaolin-based geopolymer mortars with different alkaline activators (Na + and K + )
| Autor: | Larissa Rodrigues da Costa de Oliveira Marques, Fernando Cesar Coelho França, Rafael Rangel de Salles Guerra, Thais da Silva Rocha, Dylmar Penteado Dias |
|---|---|
| Rok vydání: | 2018 |
| Předmět: |
Potassium hydroxide
Materials science Potassium 0211 other engineering and technologies chemistry.chemical_element Sodium silicate 02 engineering and technology Building and Construction 021001 nanoscience & nanotechnology Geopolymer chemistry.chemical_compound Compressive strength chemistry Chemical engineering 021105 building & construction Ultimate tensile strength General Materials Science 0210 nano-technology Metakaolin Potassium silicate Civil and Structural Engineering |
| Zdroj: | Construction and Building Materials. 178:453-461 |
| ISSN: | 0950-0618 |
| Popis: | In this study, the influence of different alkaline activators (Na+ and K+) on the mechanical, thermal, and microstructural behaviors of metakaolin-based geopolymer mortars was investigated. Four types of mortars were manufactured, and the only difference between them was the alkaline-activating solution. Potassium and alkaline sodium silicates and potassium and sodium hydroxides were used in combination as the alkaline-activating solutions. Compressive strengths, indirect tensile strengths, and longitudinal moduli of elasticity of the mortars were evaluated along with thermal property analysis (thermogravimetric analysis and differential thermal analysis) and scanning electron microscopy (SEM). All the mortars exhibited similar compressive strength, >80 MPa, at 28 days. It was possible to observe a high gain in the mechanical strength in the early ages, which is characteristic of geopolymers. The increase in mechanical strength ranged approximately from 72% to 81% after 3 days and from 86% to 93% after 7 days with respect to the strength at 28 days. Mortars produced with alkaline sodium silicate exhibited a heterogeneous microstructure with a large number of pores, while those containing potassium silicate were denser and exhibited low porosity. Such different morphologies of the mortars are a result of the type of the alkaline cations used; their effect could also be perceived in the thermal performance of the mortars, with better performance induced by potassium silicate and potassium hydroxide. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect