Influence of nanometric microstructural development on thermophysical properties of lanthanum-doped strontium titanate
| Autor: | Siti Nor Ain Rusly, Nor Hidayat Yusof, Idza Riati Ibrahim, Norni Hidayawati Mat Daud, Ismayadi Ismail, Hideki Nakajima, Narong Chanlek, Ghazaleh Bahmanrokh, Mohd Hafiz Mohd Zaid, Rodziah Nazlan, Khamirul Amin Matori |
|---|---|
| Rok vydání: | 2021 |
| Předmět: |
Materials science
Phonon scattering chemistry.chemical_element 02 engineering and technology 010402 general chemistry 021001 nanoscience & nanotechnology Condensed Matter Physics Thermal diffusivity 01 natural sciences Grain size 0104 chemical sciences chemistry.chemical_compound Grain growth chemistry Lanthanum Strontium titanate General Materials Science Grain boundary Crystallite Composite material 0210 nano-technology |
| Zdroj: | Materials Chemistry and Physics. 270:124867 |
| ISSN: | 0254-0584 |
| Popis: | The evolution of imperfect crystal from a highly amorphous structure to an ordered crystalline structure via sintering has demonstrated a significant development onto the thermophysical properties. Therefore, a series of La-doped strontium titanate with different morphological properties have been synthesized via high energy ball milling with subsequent sintering. Doping of lanthanum tends to inhibit the grain growth where a significant reduction of grain size (range from 34 nm to 0.47 μm) could be observed. A large amount of grain boundaries presence with fine grains, resulting from lanthanum doping, has enhanced phonon scattering, thus yielding a low heat propagation in La-doped SrTiO3. Besides acting as a grain growth inhibitor, lanthanum also acts as a scattering centre due to imperfection created by the doping. The scattering mechanisms significantly decrease the phonon mean free path. Consequently, the thermal diffusivity has been efficiently reduced to 1.1 mm2/s as compared to that of pure SrTiO3 which showed a value of about 3.8 mm2/s, both observed for the complete phase polycrystalline materials. The systematic development of thermophysical and morphological properties of La-doped SrTiO3 can be served as a preliminary guide to engineer thermoelectric materials with low thermal diffusivity. |