| Popis: |
In this study, the Local natural Iraqi rocks kaolin with the addition of different proportions of MgO along with its effects on the physical and thermal properties of the prepared refractories were investigated. kaolin/MgO mixture was milled and classified into various size fractions, the kaolin (less than 105 µm) and MgO (less than 50µm). The specimens were mixed from kaolin and MgO in range M1 (95+5)%, M2 (90+10) %, M3(85+15)% and M4(80+20)% respectively. The green specimens were shaped by the semi-dry method using a hydraulic press and a molding pressure of (5)Ton with addition of (9-12) %wt. of pva solution ratio. After molding and drying, the specimens were fired at (1100, 1200 and 1300)°C. Physical properties (density, porosity, Water Absorption) and thermal properties (thermal conductivity) were measured for all the prepared samples. The results showed that the porosity was increased and the density was decreased, such increase &decrease affected on to the thermal properties for refractory.In this study, the Local natural Iraqi rocks kaolin with the addition of different proportions of MgO along with its effects on the physical and thermal properties of the prepared refractories were investigated. kaolin/MgO mixture was milled and classified into various size fractions, the kaolin (less than 105 µm) and MgO (less than 50µm). The specimens were mixed from kaolin and MgO in range M1 (95+5)%, M2 (90+10) %, M3(85+15)% and M4(80+20)% respectively. The green specimens were shaped by the semi-dry method using a hydraulic press and a molding pressure of (5)Ton with addition of (9-12) %wt. of pva solution ratio. After molding and drying, the specimens were fired at (1100, 1200 and 1300)°C. Physical properties (density, porosity, Water Absorption) and thermal properties (thermal conductivity) were measured for all the prepared samples. The results showed that the porosity was increased and the density was decreased, such increase &decrease affected on to the thermal properties for refractory. |