Corrosion Behavior of Alloy A3003 After Brazing in HCl, CH3COOH, and Mixed Solutions

Autor:	Masakazu Edo, Shu Kuroda, Shohei Iwao, Michihide Yoshino
Rok vydání:	2015
Předmět:	Materials science General Chemical Engineering Alloy Metallurgy Hydrochloric acid General Chemistry engineering.material Electrochemistry Corrosion Acetic acid chemistry.chemical_compound chemistry engineering Pitting corrosion Brazing General Materials Science Polarization (electrochemistry)
Zdroj:	CORROSION. 71:598-605
ISSN:	1938-159X 0010-9312
DOI:	10.5006/1332
Popis:	Dip and dry corrosion tests were carried out on Alloy A3003 (UNS A93003) using hydrochloric acid (HCl), acetic acid (CH3COOH), and a mixed solution. After 50 corrosion test cycles with the HCl solution, pitting corrosion occurred in some parts at higher concentrations, but corrosion weight loss was very low. In the case of the CH3COOH solution, general corrosion occurred, thickness decreased, and weight loss significantly increased as the concentration grew. In the case of the mixed solution, both general corrosion and pitting corrosion occurred, and corrosion mass loss increased as the HCl concentration grew. Also, in concentrations of more than 50 ppm of HCl, the number of pits significantly increased. Electrochemical polarization measurements were done to understand the corrosion forms for each acid. In the electrochemical polarization, the pitting potential became less noble with increasing concentration of HCl. No distinct effect of CH3COOH on the pitting potential was confirmed, but corrosion curren...
Databáze:	OpenAIRE
Externí odkaz:	https://explore.openaire.eu/search/publication?articleId=doi_________::467e01d0d6df3b9b0417911c5ab09e7c https://doi.org/10.5006/1332 Zobrazit plný text záznamu