Effect of titanium dioxide and 3.5% hydrogen peroxide with 405-nm diode laser irradiation on bonding of resin to pulp chamber dentin

Autor: Yoshito Hirai, Junji Kato, Akiko Haruyama, Yutaka Oda, Atsushi Kameyama
Rok vydání: 2010
Předmět:
Zdroj: Laser Physics. 20:881-885
ISSN: 1555-6611
1054-660X
DOI: 10.1134/s1054660x10070108
Popis: This study was conducted to determine the effect of a 3.5% hydrogen peroxide solution containing titanium dioxide on bonding of resin to pulp chamber dentin. Extracted bovine anterior teeth were allocated to three groups of ten teeth each. The coronal labial pulp chamber dentin was exposed and bleached with 3.5% hydrogen peroxide with titanium dioxide with 405-nm diode laser irradiation for 15 min (Group 1); 30% hydrogen peroxide with halogen lamp irradiation for 15 min (Group 2); and distilled water for 15 min (Group 3). After bleaching, the pulp chamber dentin was prepared for composite resin bonding and the interface between the resin and dentin was observed by scanning electron microscopy. The microtensile bond strength (μTBS) and failure patterns were determined. The μTBS values (mean ± SD) were: 17.28 ± 5.79 MPa (n = 36), 0 MPa, and 26.50 ± 9.83 MPa (n = 36) in Groups 1, 2, and 3, respectively. The μTBS in Group 3 was significantly higher than that in Group 1 (P < 0.05). Hybrid layers and resin tags were clearly observed at the interface in Groups 1 and 3, but not in Group 2. Adhesive failure was mainly observed in Group 1, whereas dentin failure was the main failure pattern in Group 3.
Databáze: OpenAIRE
Externí odkaz: