Modelling creep damage in heat affected zone in 321 stainless steel. Part I: Quantitative study of intergranular damage
| Autor: | M. Mottot, M. Chabaud-Reytier, C. Cäes-Hogrel, L. Allais, D. Poquillon, André Pineau |
|---|---|
| Rok vydání: | 2001 |
| Předmět: |
Heat-affected zone
Materials science Mechanical Engineering Metallurgy Metals and Alloys Structural integrity engineering.material Intergranular corrosion Condensed Matter Physics Cracking Creep Mechanics of Materials Materials Chemistry Ceramics and Composites engineering Fracture (geology) Austenitic stainless steel |
| Zdroj: | Materials at High Temperatures. 18:71-80 |
| ISSN: | 1878-6413 0960-3409 |
| DOI: | 10.1179/mht.2001.008 |
| Popis: | During service at high temperature, stabilized stainless steels are well known to present a serious form of intergranular cracking in the Heat Affected Zones (HAZ) referred to as the reheat cracking phenomenon which is very deleterious for the structural integrity of welds made in this steel. The purpose of the present study is to present quantitative results on mechanical behaviour and the damage at high temperature of simulated HAZ which show different sensitivities to intergranular cracking. Creep laws are determined and an intergranular damage model is identified using the local approach to fracture based on mechanical tests performed at 600 °C and metallurgical observations on smooth specimens and two types of notched specimens. |