In the oxidation of TiAl alloys, the role of scale-growth stresses formed during oxidation has, thus far, been unknown. In the present paper the oxide-growth stresses were investigated by the deflection-test method in monofacial oxidation (DTMO) accompanied by acoustic-emission measurements. On unmodified surfaces the growth stresses are compressive and reach levels of around −100 MPa. At the same time, significant acoustic emission occurs indicating that even under isothermal conditions, stresses are relieved by a scale-cracking mechanism. For oxide scales on TiAl surfaces, which had been ion implanted with chlorine before oxidation, a very thin protective alumina layer is formed which, however, develops growth stresses in the range of several GPa, accompanied by intensive acoustic emission. In all stress–time curves, a dynamic situation is observed. This consists of phases of stress relief by scale microcracking and phases of stresses increase due to crack healing and further oxide growth. As a result, the level of stress as a function of oxidation time, is characterized by an oscillating course. |
Full text from SpringerLink