High work-hardening effect of the pure NiAl intermetallic compound fabricated by the combustion synthesis and hot pressing technique
| Autor: | Qi-Chuan Jiang, Hongran Zhao, Feng Qiu, Shenbao Jin |
|---|---|
| Rok vydání: | 2011 |
| Předmět: |
Nial
Materials science Mechanical Engineering Metallurgy Intermetallic Work hardening Condensed Matter Physics Microstructure Hot pressing Compressive strength Mechanics of Materials General Materials Science Dislocation High-resolution transmission electron microscopy computer computer.programming_language |
| Zdroj: | Materials Letters. 65:2604-2606 |
| ISSN: | 0167-577X |
| DOI: | 10.1016/j.matlet.2011.05.091 |
| Popis: | The pure NiAl intermetallic compound was fabricated by the combustion synthesis and hot pressing technique. Microstructure examination showed that the NiAl intermetallic compound contained fine grains. Analysis of the X-ray diffraction and the HRTEM studies showed that the phase in the intermetallics was the only NiAl phase. The NiAl showed prominent compression properties. The true ultimate compression strength and the fracture strain of the NiAl are 1002 − 94 + 72 MPa and 21.6 − 1.8 + 1.8 %, respectively. The work-hardening capacity ( H c ) is 1.40 − 0.07 + 0.09 and the Vickers micro-hardness is 360 − 19 + 15 HV. The finer grains, the high density dislocation and the seriously distorted lattices in the matrix, and the intense interactions between dislocations contribute to the prominent compression properties. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect