After a maturation of three days at ambient temperature, the sulfur-prevulcanized natural rubber latex (SNRL) was stabilized by 20wt% Peregal O, and then acidified with the 36wt% acetic acid by a ratio of 5, 15, 25, 35 and 45 g of 36wt% acetic acid to 100g SNRL, to obtain acidified prevulcanized NR latex (ASNRL) with different acidity, respectively. The viscosity of ASNRL increased, while the nitrogen content decreased, with the increment of acetic acid content and the decrease in pH; for unaged samples, the tensile strength, elongation at break, 300% and 500% moduli of the ASNRL films were only slightly lower than those of SNRL film; however the hot-air aging resistance decreased with the increment of acetic acid content. |