Preparation of LaFe12ONO19 by coprecipitation method to reduce the sintering time
| Autor: | Dario Bueno-Baques, R. Grossinger, José Andrés Matutes-Aquino, M. Kupferling, Veronica Corral-Flores |
|---|---|
| Rok vydání: | 2006 |
| Předmět: |
Quenching
Materials science Coprecipitation Annealing (metallurgy) Mechanical Engineering Metal ions in aqueous solution Metallurgy Sintering Industrial and Manufacturing Engineering Magnetization Ammonium hydroxide chemistry.chemical_compound chemistry Mechanics of Materials Safety Risk Reliability and Quality Saturation (magnetic) Nuclear chemistry |
| Zdroj: | International Journal of Materials and Product Technology. 27:124 |
| ISSN: | 1741-5209 0268-1900 |
| DOI: | 10.1504/ijmpt.2006.010679 |
| Popis: | LaFe12ONO19 was synthesised by the coprecipitation method. The preparation involved the precipitation of the metal ions from a nitrate solution in the presence of ammonium hydroxide, followed by a digestion step at 80°C. The La:Fe ratio was fixed at 1:8 in order to compensate La losses. The precipitated powder was carefully washed, filtered and dried prior to its oxidation at 800°C for 24 hours. Pressed samples were annealed at several temperatures and times, and rapidly quenched to preserve the LaFe12ONO19 phase. The study of the annealing temperature revealed a shift of the stability range to lower temperatures. 1375°C was fixed to find the influence of the sintering time over the La hexaferrite formation. The sintering time required to obtain La hexaferrite was found to be as short as 5 minutes, which is significantly lower than the one reported before (24–29 hours); however, the highest saturation magnetisation was obtained at 8 hours. |