High capacity and performance lithium based electrochromic device via amorphous tantalum oxide protective layer
| Autor: | Yingchun He, Qianqian Zhang, Fan Zhang, Xungang Diao, Guobo Dong, Xiaolan Zhong |
|---|---|
| Rok vydání: | 2018 |
| Předmět: |
Materials science
General Chemical Engineering Nickel oxide 02 engineering and technology Electrolyte 010402 general chemistry 021001 nanoscience & nanotechnology Electrochemistry Electrochromic devices 01 natural sciences 0104 chemical sciences Amorphous solid Chemical engineering Electrochromism Transmittance 0210 nano-technology Leakage (electronics) |
| Zdroj: | Electrochimica Acta. 280:163-170 |
| ISSN: | 0013-4686 |
| Popis: | Electrochromic devices (ECDs) composed tungsten oxide (WOx) and nickel oxide (NiOx) films have attracted extensive attention due to the high transmittance contrast, the short response time and the low power consumption which represent a better prospect of applications. Even though a lot of efforts have been made to improve the stabilities and the cycling life of the ECDs, however, the effects are unsatisfactory, because the physical mechanisms of the degenerate properties are still not clear. Meanwhile, an easy processing and low cost manufacture method by composing functional devices are still insufficient. We hereby present an effective method to obtain a high capacity and performance lithium based ECDs by using of amorphous tantalum oxide (Ta2O5) protective layers, which can be used to improve the surface morphologies of NiOx films, effectively protect the films from the slightly acid environment of the electrolyte and reduce the leakage. Five-layer structures ECD1 (ITO/NiOx/Li+ based gel polymer electrolyte/WOx/ITO) and six-layer structures ECD2 (ITO/NiOx/Ta2O5/Li+ based gel polymer electrolyte/WOx/ITO) are prepared by special laminated glass method. Through the measurement of surface morphology and surface structure, as well as the electrochemical and spectral characterization, the charge capacity of NiOx with the optimized Ta2O5 film increases by 38% compared with the pure NiOx film. Also, the Ta2O5 film is helpful to enlarge the transmittance contrast, decrease the peak current of potential switch and electrochemical impedance. In the present of the protective layer, the ECD2 shows better bleached state (72%), higher coloration efficiency (66.2 cm2/C) and most importantly, better cyclic stability. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect