Energetics of Nanoarchitectured TiO2−ZrO2 and TiO2−MoO3 Composite Materials

Autor:	S. H. Elder, M. R. Ranade, A. Navrotsky
Rok vydání:	2002
Předmět:	Anatase Materials science General Chemical Engineering Sodium molybdate Enthalpy Analytical chemistry General Chemistry Calorimetry Nanocrystalline material Amorphous solid Enthalpy change of solution Crystallography chemistry.chemical_compound chemistry Materials Chemistry Mesoporous material
Zdroj:	Chemistry of Materials. 14:1107-1114
ISSN:	1520-5002 0897-4756
Popis:	High-temperature drop solution calorimetry in sodium molybdate solvent was performed on nanoarchitectured materials using a Calvet twin microcalorimeter at 975 K. Nanocrystalline TiO2−ZrO2 samples (mesoporous structure) and nanocrystalline TiO2−MoO3 samples (core−shell structure) were investigated. With the use of the measured drop solution enthalpies, the transformation enthalpies to macroscopic stable crystalline phases have been calculated. The enthalpy of transformation from amorphous to monoclinic ZrO2 obtained from this work, −50.08 ± 4.92 kJ/mol, is in reasonable agreement with the value of −58.60 ± 3.30 kJ/mol determined by Molodetsky et al. (2000). The enthalpy of transformation from amorphous to crystalline MoO3 derived from these data is −51.25 ± 2.01 kJ/mol. The enthalpy of transformation of nanophase anatase to bulk macrocrystalline rutile TiO2 is −7.02 ± 0.96 kJ/mol. The linear variation of energetics with the composition of both series, TiO2−ZrO2 and TiO2−MoO3, suggests that these materials...
Databáze:	OpenAIRE
Externí odkaz:	https://explore.openaire.eu/search/publication?articleId=doi_________::35cd52fb470d74294c14bdb51184f304 https://doi.org/10.1021/cm010607u Zobrazit plný text záznamu