6CrW2MoVSi steel has a refined and even microstructure after heat treatment, the average size of annealing carbide is 0.6 μm; quenching martensite is mainly lath-shaped martensite and only a small amount of acicular martensite, and the size of quenching acicular at 950 °C is smaller than 2.5 μm. The curve of quenching hardness increasing with quenching temperature rising is divided into three sections. In the middle section of quenching between 910 °C ~ 980 °C, quenching hardness presents slow rising trend. After higher temperature quenching, there are low and high temperature tempering precipitation hardening zones. At 220 °C ~ 240 °C tempering temperature, precipitation hardness is HRC54 ~ 58. At 540 °C ~ 570 °C tempering temperature, precipitation hardness is HRC52 ~ 56. |