Light Burning Condition of Preparing Dolomite Clinker Using Natural Dolomite

Autor: Wang Nian Zhang, Xi Tang Wang, Zhou Fu Wang
Rok vydání: 2018
Předmět:
Zdroj: Solid State Phenomena. 281:156-162
ISSN: 1662-9779
DOI: 10.4028/www.scientific.net/ssp.281.156
Popis: The influence of the light burning temperature on the sintering property of nature dolomite has been investigated by two-step sintering process in the temperature range 1500 °C to 1600 °C. The resulting bulk densities and apparent porosities of the sintered dolomite samples were examined, and analyzing the sintered dolomite by scanning electron microscopy and X-ray diffraction were performed. The results showed light burned at 850 °C for 3 h, the main phases of the dolomite with 3-5 grain size were MgO, CaO and little CaCO3, and then fired at 1600 °C,the density of sintering dolomite reached to 3.38 g/cm3, the apparent property was 1.2 %, the size of MgO grain up to 3.75 μm . However when dolomite light burned at 1050 °C for 3 h, the main phases were MgO and CaO, and then fired at 1600 °C,the density of sintering dolomite only was 3.30 g/cm3, the apparent property was 2.3 %, the size of MgO only was 3.05 μm .
Databáze: OpenAIRE