| Popis: |
A ninety-day aging study was performed on Halthane 73-18A to determine the thermal aging effects due to the presence of DABCO, a catalyst. Samples were taken after 14 days, 30 days, 60 days, and 90 days of exposure to air at 90/sup 0/C. Tests used to evaluate aging effects were: ring tensile, differential scanning calorimetry, dynamic dielectric spectroscopy, and solvent swell. Results of tensile tests indicated an increase in tensile properties that peaked at 30 days and decayed to 70 percent loss of peak strength in 90 days. DSC, DDS, and solvent swell data all followed the same trend. Comparative analysis of all data support the hypothesis that the presence of DABCO increases the oxidative cleavage of the polyether chain segment. |