Change in pore structure of yttria-stabilized zirconia during sintering
| Autor: | S. V. Gabelkov, A. G. Mironova, R. V. Tarasov |
|---|---|
| Rok vydání: | 2011 |
| Předmět: |
Materials science
Metals and Alloys Sintering Activation energy Atmospheric temperature range Condensed Matter Physics Crystallography Volume (thermodynamics) Chemical engineering Mechanics of Materials Agglomerate Materials Chemistry Ceramics and Composites Cubic zirconia Yttria-stabilized zirconia Solid solution |
| Zdroj: | Powder Metallurgy and Metal Ceramics. 50:151-156 |
| ISSN: | 1573-9066 1068-1302 |
| DOI: | 10.1007/s11106-011-9312-2 |
| Popis: | The behavior of coarse and fine pore channels and closed pores (pore space components) in temperature ranges of intensive (900–1150°C) and less active (1150–1400°C) sintering of a sample pressed from nanosized powder of tetragonal zirconia solid solution is examined. The change in the volume of the sample in the temperature range of intensive sintering is determined by approximately equal decrease in the volume of coarse and fine pore channels, which originate from channels between agglomerates and between aggregates in the powder agglomerates. Closed pores of the sample originating from closed pores of the powder make a minor contribution to the decrease in volume since they contain air. In the temperature range of less active sintering, all fine (200–300 nm) and coarse (0.8–1 μm) pore channels are broken and new closed pores are formed. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full text from SpringerLink