Magnetization and transport properties of silver-sheathed (Hg, Re)Ba2Ca2Cu3O8 tapes
| Autor: | J.H. Su, P.V.P.S.S. Sastry, Justin Schwartz |
|---|---|
| Rok vydání: | 2003 |
| Předmět: |
Diffraction
Superconductivity Materials science Condensed matter physics Scanning electron microscope Metals and Alloys Condensed Matter Physics Power law Vortex Magnetization Hysteresis Condensed Matter::Superconductivity Materials Chemistry Ceramics and Composites Electrical and Electronic Engineering FOIL method |
| Zdroj: | Superconductor Science and Technology. 16:1134-1138 |
| ISSN: | 1361-6668 0953-2048 |
| DOI: | 10.1088/0953-2048/16/10/302 |
| Popis: | (Hg, Re)Ba2Ca2Cu3O8+δ ((Hg, Re)-1223) samples have been fabricated by wrapping Re0.2Ba2Ca2Cu3Oy precursor powder within Ag foil and pressing or rolling. The Ag/precursor composite is then reacted with CaHgO2 in sealed reaction tubes. X-ray diffraction (XRD) patterns showed only one superconducting phase, (Hg, Re)-1223, in agreement with magnetization measurements showing an onset critical temperature (Tc) of 132 K. The magnetization properties were studied by dc magnetic measurements. The irreversibility line (Hirr), deduced from magnetization hysteresis loops, is approximated by a power law, Hirr ~ (1 − T/Tc)n, with n ~ 2.5, indicating moderate coupling between CuO2 layers compared to YBa2Cu3O7 (n ~ 1.5) and Bi/Tl-based superconductors (n ~ 5.5). The temperature dependence of the magnetization hysteresis loop width ΔM showed three regimes, dominated by weak links at low temperature (regime I), thermally activated depinning of vortices at intermediate temperature (regime II) and giant flux creep at high temperature (regime III), respectively. Two field dependences were found in the intragrain critical current density (Jmagc) versus applied field at various temperatures: a weak one at lower temperature (≤50 K) and a stronger one at high temperature (≥65 K), indicating a transition from vortex lattice to vortex liquid in the tapes. The transport critical current density (Jtranc) of ~3 × 103 A cm−2 at 4.2 K and self-field was comparable to those for bulk Hg-based superconductors, indicating granular nature of the samples, which was confirmed further by XRD, scanning electron microscopy (SEM) and magneto-optical imaging (MOI). |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|