High-efficiency simultaneous extraction of rare earth elements and iron from NdFeB waste by oxalic acid leaching
| Autor: | Xuezhong Wang, Hua-jin Cheng, Hao Guo, Tao Tu, Qingsheng Liu |
|---|---|
| Rok vydání: | 2021 |
| Předmět: |
Electrolysis
Aqueous solution Inorganic chemistry Oxalic acid Oxide 02 engineering and technology General Chemistry 010402 general chemistry 021001 nanoscience & nanotechnology 01 natural sciences Ferric oxalate Oxalate 0104 chemical sciences Ferrous law.invention chemistry.chemical_compound chemistry Geochemistry and Petrology law Leaching (metallurgy) 0210 nano-technology |
| Zdroj: | Journal of Rare Earths. 39:323-330 |
| ISSN: | 1002-0721 |
| DOI: | 10.1016/j.jre.2020.04.020 |
| Popis: | Iron can not be recovered at high value because only rare earth elements are effectively recovered from NdFeB waste via oxidation roasting-hydrochloric acid leaching process. In this study, a new method for leaching NdFeB waste with oxalic acid was developed. The high-efficiency, simultaneous and high-value recovery of rare earth elements and iron was realized to simplify the process and improve the economic benefit. Results of the oxalic acid leaching experiments show that under the optimum leaching conditions at 90 °C for 6 h in the aqueous solution of oxalic acid (2 mol/L) with a liquid–solid ratio of 60 mL/g, the iron leaching efficiency and precipitation rate of rare earth oxalate reach 93.89% and 93.17%, respectively. Rare earth oxalate and Fe(C2O4)33− were left in the residue and the leaching solution, respectively. The leaching mechanism was further analyzed by characterising the leach residues obtained through X-ray powder diffraction (XRD) and scanning electron microscopy-energy dispersive X-ray spectroscopy (SEM-EDS). Results of the leaching kinetics study indicate that the process of oxalic acid leaching follows the shrinking nucleus model, and the leaching kinetics model is controlled by the mixed factors of diffusion and chemical reaction. The leaching residue was calcined at 850 °C for 3 h and then decomposed into rare earth oxide, which can be directly used to prepare rare earth alloy via molten salt electrolysis. For the leaching solution, ferric oxalate solution was reduced using Fe powder to prepare the ferrous oxalate (FeC2O4·2H2O). |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect