Synthesis of carboxymethyl-chitosan/acrylic acid hydrogel using silane crosslinker
| Autor: | Nadia Rasool, Zareen Akhter, Tariq Yasin |
|---|---|
| Rok vydání: | 2008 |
| Předmět: |
Thermogravimetric analysis
Materials science Aqueous solution Vinyltriethoxysilane Polymers and Plastics General Chemical Engineering Silane Chitosan chemistry.chemical_compound chemistry Self-healing hydrogels Polymer chemistry medicine Physical and Theoretical Chemistry Swelling medicine.symptom Acrylic acid Nuclear chemistry |
| Zdroj: | e-Polymers. 8 |
| ISSN: | 1618-7229 2197-4586 |
| Popis: | Novel pH sensitive carboxymethyl (CM) chitosan/acrylic acid hydrogels were prepared. CM-chitosan and acrylic acid (AA) in aqueous solution were copolymerized and crosslinked by using vinyltriethoxysilane (VTESi). Different amounts of AA and crosslinker were incorporated in CM-chitosan/AA hydrogel. IR analysis confirmed the presence of pyranose ring as well as Si-O-Si linkage within the hydrogel. Thermogravimetric analysis showed an increase in the stability of hydrogel either having high AA ratio or high crosslinker ratio. The swelling of the hydrogels was carried out by investigating the effect of time, pH (buffered and nonbuffered) and ionic media. In non-buffered media the overall swelling was found to be high as compared to buffered media. Maximum swelling was observed in hydrogel having mass ratio of 7.0 (AA : CM-chitosan). This hydrogel showed low swelling in low pH similar to that of the stomach and high swelling in neutral pH similar to that of the small intestine and can be used in drug delivery applications |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|