Amorphous-to-Crystalline Transformation in Evaporated FeSi Films

Autor: W. A. Theiner, S. K. Sharma, H. P. Geserich
Rok vydání: 1975
Předmět:
Zdroj: Physica Status Solidi (a). 32:467-474
ISSN: 1521-396X
0031-8965
DOI: 10.1002/pssa.2210320215
Popis: Thin films of FeSi deposited at room temperature showed amorphous structure. Amorphous-to-crystalline transformation in these films has been investigated using electron microscopy and diffraction techniques. Differential thermoanalysis (DTA) studies of the films showed an exothermic reaction peak at this transformation. Using DTA thermographs the energy of reaction has been calculated and is equal to 1.8 kcal/mol. Measurements on the electrical conductivity of these films have also been made and they also revealed a transformation around the same temperature which was observed by DTA and electron microscopy and diffraction investigations. An dunnen FeSi-Schichten, die bei Raumtemperatur abgeschieden wurden und amorph waren, wurde die Transformation amorph-kristallin mit Hilfe von Elektronenmikroskopie und -beugung untersucht. Differentialthermoanalyse (DTA) der Schichten ergab bei der Transformation eine exotherme Reaktion. Die Reaktionsenergie wurde aus den DTA-Daten zu 1,8 kcal/Mol berechnet. Messungen der elektrischen Leitfahigkeit der Schichten deuten ebenfalls auf eine Transformation bei der gleichen Temperatur hin, wie sie mit DTA, Elektronenmikroskopie und -beugung beobachtet wurde.
Databáze: OpenAIRE
Externí odkaz: