Polyacrylonitrile‐Based Electrolytes with Ternary Solvent Mixtures as Plasticizers
| Autor: | D. Peramunage, K. M. Abraham, D. M. Pasquariello |
|---|---|
| Rok vydání: | 1995 |
| Předmět: |
Renewable Energy
Sustainability and the Environment Inorganic chemistry Polyacrylonitrile Analytical chemistry Order (ring theory) chemistry.chemical_element Electrolyte Condensed Matter Physics Mole fraction Surfaces Coatings and Films Electronic Optical and Magnetic Materials chemistry.chemical_compound Nickel chemistry Propylene carbonate Materials Chemistry Electrochemistry Platinum Ethylene carbonate |
| Zdroj: | Journal of The Electrochemical Society. 142:1789-1798 |
| ISSN: | 1945-7111 0013-4651 |
| DOI: | 10.1149/1.2044195 |
| Popis: | Polyacrylonitrile (PAN)-based electrolytes with improved low temperature conductivity can be prepared using carefully selected plasticizer composition from ternary solvent mixtures consisting of propylene carbonate (PC), ethylene carbonate (EC), and butylene carbonate (BC) or PC, EC, and 3-methyl-2-oxazolidinone (MEOX). All the electrolytes were prepared as freestanding films. A number of solid polymer electrolyte compositions potentially useful for ambient temperature applications were identified. The solid polymer electrolyte composition with 21.0 mole percent (m/o) PAN:37.8 m/o EC:22.9 m/o PC:12.3 m/o BC:6.0 m/o LiAsF{sub 6} exhibited conductivities of 1.12 {times} 10{sup {minus}4} S/cm at {minus}40 C and 2.88 {times} 10{sup {minus}3} S/cm at 25 C. Cyclic voltammetry of the electrolytes on Al indicated small oxidative currents of the order of 0.5 {micro}A/cm{sup 2} at 4.2 V vs. Li{sup +}/Li. Pt, Ni, and carbon showed oxidative currents of the order of 1, 30, and 60 {micro}A/cm{sup 2}, respectively, at the same potential. Alloy formation and plating were evident on Al at 0.15 and {minus}0.20 V, respectively. Platinum showed similar behavior with alloy formation at 0.45 V and Li plating at 0.05 V. Carbon showed an onset of Li intercalation around 1.5 V followed by Li plating at {minus}0.1 V. Nickel showed a simple Li plating-strippingmore » process at {minus}0.05 and 0.15 V vs. Li{sup +}/Li, respectively. The rechargeability of the Li/solid polymer electrolyte/Li{sub 0.8}Mn{sub 2}O{sub 4} cell showed short cycle life in electrolytes containing BC with cell failure caused by internal soft shorts on charge. In contrast, cells with MEOX-containing polymer electrolytes showed vastly improved cyclability. A typical cell retained more than 80% of the second cycle capacity through 140 cycles at 0.1 mA/cm{sup 2}.« less |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|