It is plausible to assume that epitaxy is a special case of heterogeneous nucleation in which a restrictive crystallographic relationship exists between substrate and deposit orientations. This would mean that epitaxial substrates should always induce a perceptible reduction in the critical supercooling for nucleation of the deposit. To test this hypothesis, the critical supercoolings of six organic compounds were measured on glass and 11 single-crystal cleaved substrates including (0001) graphite, (001) mica, (111) BaF2, SrF2, and CaF2, and (100) KCl, KBr, KI, NaCl, NaF, and LiF. Reductions in supercooling (with reference to glass substrates) were checked many times for repeatability and reproducibility and shown in almost all cases to have a standard deviation of 1 C or less. Acetanilide, benzoic acid, and p-bromochlorobenzene showed a wide range of supercooling reductions and were oriented on all crystalline substrates. Naphthalene and p-dibromobenzene showed only slight supercooling reductions but were oriented on all substrates, including glass. Benzil showed strong supercooling reductions only for mica and KI but was oriented not only in these cases but also with KI, BaF2, CaF2, and graphite. There was little correlation between degree of lattice match and either supercooling reduction or degree of preferred orientation. These results suggest that, for the systems and geometry studied, forces such as molecular dipole binding and growth anisotropy had a stronger effect than lattice match. |
Full Text from ScienceDirect