Crack tip opening angle measurement through a girth weld in an X100 steel pipeline section*
| Autor: | Joseph D. McColskey, Philippe P. Darcis, Christopher N. McCowan, Richard J. Fields |
|---|---|
| Rok vydání: | 2008 |
| Předmět: |
Heat-affected zone
Materials science business.industry Mechanical Engineering Crack tip opening displacement Fracture mechanics Welding Structural engineering Crack growth resistance curve Girth (geometry) law.invention Mechanics of Materials law Perpendicular Fracture (geology) General Materials Science business |
| Zdroj: | Fatigue & Fracture of Engineering Materials & Structures. 31:1065-1078 |
| ISSN: | 1460-2695 8756-758X |
| DOI: | 10.1111/j.1460-2695.2008.01297.x |
| Popis: | Crack tip opening angle (CTOA) is becoming one of the most accepted methods for characterizing fully plastic fracture. It provides a measure of the resistance to fracture for a material in cases where there is a large degree of stable-tearing crack extension during the fracture process. Our current pipeline research uses the CTOA test as an alternative, or addition, to the CTOD (crack tip opening displacement) and the fracture energy characterization provided by the J-integral approach. A test technique was developed for measurement of CTOA that uses a modified double cantilever beam (MDCB) specimen. A digital camera and image analysis software were used to record the progression of the crack tip and to estimate the CTOA. In this article, CTOA data on crack growth orientations perpendicular to pipeline girth welds are presented. The CTOA for X100 high strength bainitic gas pipeline steel is reported. Two different specimen gauge sections, 3 mm and 8 mm, were used and the effect of the specimen thickness on the CTOA is discussed. The results show a change in the CTOA as the crack grows into the heat affected zone (HAZ). A slight improvement in the fracture resistance is measured, and through the weld, a slight decrease in fracture resistance is observed. |