Materials science business.product_category Polymers and Plastics Annealing (metallurgy) General Chemical Engineering Molding (process) engineering.material Polyester Isophthalic acid chemistry.chemical_compound chemistry Butanediol Coating Polymer chemistry engineering Die (manufacturing) business |
| Zdroj: | Acta Polymerica. 41:473-475 |
| ISSN: | 1521-4044 0323-7648 |
| DOI: | 10.1002/actp.1990.010410901 |
| Popis: | The shrinkage of copolyesters from terephthalic acid, isophthalic acid, and butanediol during injection molding and the after-shrinkage during annealing exhibits a minimum at 20 mole-% isophthalic acid. Polyesters of this composition have proved to be new outstanding materials for secondary coating of quartz glass optical fibres. They allow the production of optical fibre constructions without any increase in optical damping down to − 50°C. Die Schwindung beim Spritzgus und Nachschwindung beim Tempern von Copolyestern aus Terephthalsaure und Isophthalsaure mit Butandiol-1,4 weist bei einem Isophthalsauregehalt von 20 Mol-% ein Minimum auf. Polyester dieser Zusammensetzung sind neue hervorragende Materialien fur die Sekundarbeschichtung von Festader-Lichtwellenleitern. Sie erlauben die Herstellung von Festaderkonstruktionen ohne Veranderung der optischen Dampfung bis − 50°C. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Plný text