| Popis: |
During long-term and high temperature service, microstructures of superalloys may change and then have an adverse impact on mechanical properties, so the stabilities of a wrought Ni-base superalloy aging without stress at 650°C were investigated in this paper. The results showed that the size and morphology of γ' precipitates in the alloy were not obviously influenced with the increase of exposure time, and primary MC carbides present excellent thermal stability. Moreover, almost no detrimental phase was found. Tensile strength and plasticity at room temperature after aging remained steady. Under the condition of 650°C/823MPa, the stress ruptures life presented increasing trend overall and plasticity decreases slightly. In conclusion, the experiment alloy presents a good thermal stability at 650°C. |