Resist substrate studies for LIGA microfabrication with application to a new anodized aluminum substrate
| Autor: | D. M. Skala, Stewart K. Griffiths, Nancy Y. C. Yang, Georg Aigeldinger, L L Hunter, Dale R. Boehme, John T. Hachman, Thomas A. Friedmann, Cheryl A. Hauck, P C Y Yang, J S Korellis, Dorrance E. McLean, Matthew W. Losey, Michelle A. Hekmaty, Wei-Yang Lu, James J. Kelly |
|---|---|
| Rok vydání: | 2005 |
| Předmět: | |
| Zdroj: | Journal of Micromechanics and Microengineering. 15:1700-1712 |
| ISSN: | 1361-6439 0960-1317 |
| Popis: | Resist substrates used in the LIGA process must provide high initial bond strength between the substrate and resist, little degradation of the bond strength during x-ray exposure, acceptable undercut rates during development and a surface enabling good electrodeposition of metals. Additionally, they should produce little fluorescence radiation and give small secondary doses in bright regions of the resist at the substrate interface. To develop a new substrate satisfying all these requirements, we have investigated secondary resist doses due to electrons and fluorescence, resist adhesion before exposure, loss of fine features during extended development and the nucleation and adhesion of electrodeposits for various substrate materials. The result of these studies is a new anodized aluminum substrate and accompanying methods for resist bonding and electrodeposition. We demonstrate the successful use of this substrate through all process steps and establish its capabilities via the fabrication of isolated resist features down to 6 µm, feature aspect ratios up to 280 and electroformed nickel structures at heights of 190 to 1400 µm. The minimum mask absorber thickness required for this new substrate ranges from 7 to 15 µm depending on the resist thickness. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|