Sol-gel synthesis and characterization of ZnAl2O4 powders for transparent ceramics
| Autor: | Maksim Boldin, A.V. Belyaev, A.A. Murashov, N.I. Kirillova, N.M. Khamaletdinova, Stanislav Balabanov, M.I. Lelet |
|---|---|
| Rok vydání: | 2019 |
| Předmět: |
Materials science
Sintering 02 engineering and technology Hot pressing 01 natural sciences law.invention chemistry.chemical_compound law 0103 physical sciences Materials Chemistry Calcination Ceramic Sol-gel 010302 applied physics Transparent ceramics Process Chemistry and Technology Aluminium isopropoxide 021001 nanoscience & nanotechnology Surfaces Coatings and Films Electronic Optical and Magnetic Materials Chemical engineering chemistry visual_art Vickers hardness test Ceramics and Composites visual_art.visual_art_medium 0210 nano-technology |
| Zdroj: | Ceramics International. 45:4835-4839 |
| ISSN: | 0272-8842 |
| DOI: | 10.1016/j.ceramint.2018.11.179 |
| Popis: | The sol-gel synthesis of ZnAl2O4 ceramic powders from alkoxide and acetate sources of metals, as well as the microstucture and the hardness of the hot-pressed ZnAl2O4 specimens were considered. ZnAl2O4 powders were prepared by the hydrolysis of an alcohol solution of aluminium isopropoxide using an aqueous solution of zinc acetate followed by heat treatment. The thermal evolution of the ZnAl2O4 precursor was investigated. The effect of calcination temperature on the morphology and the specific surface area of ZnAl2O4 powders were also studied. The sintering of the resultant powders to the high transparent ceramic using a hot pressing with 1 wt% ZnF2, as a sintering additive was successfully demonstrated. The in-line transmittance of ZnAl2O4 ceramics (1 mm thickness) achieved 80% in the visible region and 85% at 5 µm; Vickers hardness was 11.6 GPa. |