Influence of pH values on tin sulfide films deposited on copper substrates by CBD
| Autor: | M. M. Oropeza-Saucedo, F.G. Nieto-Caballero, N. R. Silva-González, Crisoforo Morales, A. Coyopol, Godofredo García, J. M. Gracia-Jiménez, Enrique Rosendo, T. Díaz-Becerril, R. Galeazzi, R. Romano-Trujillo |
|---|---|
| Rok vydání: | 2019 |
| Předmět: |
010302 applied physics
Morphology (linguistics) Materials science Analytical chemistry chemistry.chemical_element Condensed Matter Physics 01 natural sciences Copper Atomic and Molecular Physics and Optics Electronic Optical and Magnetic Materials Crystal symbols.namesake chemistry Molecular vibration 0103 physical sciences symbols Orthorhombic crystal system Electrical and Electronic Engineering Raman spectroscopy Deposition (law) Chemical bath deposition |
| Zdroj: | Journal of Materials Science: Materials in Electronics. 30:16439-16445 |
| ISSN: | 1573-482X 0957-4522 |
| DOI: | 10.1007/s10854-019-02018-0 |
| Popis: | In this work, SnS films were deposited on copper substrates under different pH values by chemical bath deposition. The pH values were varied from 8.44 to 11.26 and SnS films were obtained at 10.62. Films of Sn6O4(OH)4 were obtained for pH values lower than 10.62 and mixed phases of SnS and Sn2S3 were formed at pH 11.26. The deposition parameters were 70 °C for 3 h for all samples. Structural, morphological and optical properties were analyzed by XRD, SEM and UV–Vis–NIR respectively. In addition, vibrational modes for Sn6O4(OH)4 and SnS films were identified by Raman spectroscopy from 60 to 380 cm−1. SnS films exhibited an orthorhombic structure and a crystal size of 15 nm. The morphology of the films was transformed from pyramidal to rice shape as the pH was increased. Gap value for Sn6O4(OH)4 films was found to be 3.11 eV and for SnS was 1.17 eV, however, for mixed SnS and Sn2S3 films the gap value was 0.61 eV. The thickness of SnS films was around 1.7 micrometers, which is an appropriate value for solar cells applications as absorber material. |