SRF test facility for the superconducting LINAC 'RAON' — RRR property and e-beam welding

Autor: Mijoung Joung, Yoochul Jung, Myungook Hyun, Jongdae Joo
Rok vydání: 2015
Předmět:
Zdroj: Journal of the Korean Physical Society. 66:454-458
ISSN: 1976-8524
0374-4884
DOI: 10.3938/jkps.66.454
Popis: Equipment, such as a vacuum furnace, high pressure rinse (HPR), eddy current test (ECT) and buffered chemical polishing (BCP), are installed in the superconducting radio frequency (SRF) test facility. Three different sizes of cryostats (diameters of 600 mm for a quarter wave resonator (QWR), 900 mm for a half wave resonator (HWR), and 1200 mm for single spoke resonator 1&2 (SSR 1&2)) for vertical RF tests are installed for testing cavities. We confirmed that as-received niobium sheets (ASTM B393, RRR300) good electrical properties because they showed average residual resistance ratio (RRR) values higher than 300. However, serious RRR degradation occurred after joining two pieces of Nb by e-beam welding because the average RRR values of the samples were ∼179, which was only ∼60% of as-received RRR value. From various e-beam welding experiments in which the welding current and a speed at a fixed welding voltage were changed, we confirmed that good welding results were obtained at a 53 mA welding current and a 20-mm/s welding speed at a fixed welding voltage of 150 kV.
Databáze: OpenAIRE
Externí odkaz: