Physical Characteristics and Compressive Strength of Na-Geopolymer Paste Designed by a Taguchi Method
| Autor: | Zainab Zayer Hassan, Mohammad A. Ahmed Al-dujaili, Imad Ali Disher Al-Hydary |
|---|---|
| Rok vydání: | 2021 |
| Předmět: | |
| Zdroj: | IOP Conference Series: Earth and Environmental Science. 877:012036 |
| ISSN: | 1755-1315 1755-1307 |
| DOI: | 10.1088/1755-1315/877/1/012036 |
| Popis: | Geopolymer paste is a revolutionary building material that the chemical activity of inorganic molecules will create. It is an alternative to traditional Portland cement and is more Eco-friendly. This analysis aimed to classify the mixtures and their process parameters suitable for the development of Geo-polymer paste with one of the ultimate compressive powers, the highest-lowest porosity, and the lowest-lowest final and initial setting time. In the experimental design of the Geo-polymer-based-metakaolin, a Taguchi methodology has been utilized. Five variables parameters were chosen that are mostly to influence the properties of the geopolymer. These are the quantity of Si, alkali, the proportion of alkali reagents, duration of blending, and water amount. These variables’ influence has been calculated at 7 and 28 days on compressive strengths, porosity, density, and setting time. The analysis indicates that the strong compressive strength (115MPa) of Geopolymer paste could be achieved with the formula (1Na2O. Al2O3. 3.8SiO2.xH2O) utilizing suitable processing conditions under which the molar ratio of alkali silicate to alkali hydroxide must be held within the range of 3.25-3.02. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|