Microstructure and properties of microarc oxidation coating formed on aluminum alloy with compound additives nano-TiO2 and nano-ZnO
| Autor: | Zhang Junjie, Ting-Yi Lin, Xiaoyan Zhang, Gong Xiangpeng, Xie-Jun Hu, Huang Xin |
|---|---|
| Rok vydání: | 2017 |
| Předmět: |
Materials science
020502 materials Metallurgy Alloy Metals and Alloys chemistry.chemical_element 02 engineering and technology Electrolyte engineering.material 021001 nanoscience & nanotechnology Condensed Matter Physics Microstructure Corrosion 0205 materials engineering chemistry Coating Aluminium Phase (matter) Nano Materials Chemistry engineering Physical and Theoretical Chemistry Composite material 0210 nano-technology |
| Zdroj: | Rare Metals. 37:976-982 |
| ISSN: | 1867-7185 1001-0521 |
| DOI: | 10.1007/s12598-017-0948-z |
| Popis: | In this work, microarc oxidation (MAO) technology was used to form oxide ceramic coating on the surface of aluminum alloy. The combined additives nano-TiO2 and nano-ZnO were added into the silicate electrolyte, and the effect of the compound nano-additive on microstructure and properties of MAO coating was investigated. The results show that compared with those of the nano-additive-free coating formed on aluminum alloy, the thickness, hardness, abrasion resistance and corrosion resistance of the nano-additive-containing coating are obviously improved. The surface of coating with nano-additive becomes smooth, dense, and there are less porosities and microcracks. Moreover, the content of crystal phase α-Al2O3 and γ-Al2O3 increases visibly on the nano-additive-containing MAO coatings, and new phases Al3Ti and Zn0.6Ti0.4 are detected in the coatings, which are mainly contributed to the excellent corrosion resistance and abrasion resistance of the film. When the contents of nano-TiO2 and nano-ZnO are, respectively, 4 and 2 g·L−1, the film has better comprehensive performance, the thickness and hardness of the film could reach 52 μm and HV 692, respectively. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full text from SpringerLink