Nitruración gaseosa a elevada temperatura de la aleación Ti6Al4V para mejorar su resistencia al desgaste
| Autor: | King, Eleanor, Fernández González, J., de Damborenea González, Juan J., Ruiz Fernández, José |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2000 |
| Předmět: | |
| Zdroj: | Revista de Metalurgia, Vol 36, Iss 6, Pp 403-409 (2000) |
| ISSN: | 1988-4222 0034-8570 |
| Popis: | TiN coatings have been successfully produced on Ti6Al4V alloy by gas nitriding in order to modify surface properties. Several characteristics of the coatings relevant to their applications in total joint replacement have been studied. Wear resistance and hardness were improved dramatically for nitrided samples compared with those un-nitrided. Substrate adhesion of the coating was studied by means of a three point bend test system. Characterisation of the TiN layer was carried by optical microscopy, SEM and XRD. Vickers hardness values up to 700 were obtained.Mediante nitruración gaseosa a elevada temperatura de la aleación Ti6Al4V se han obtenido capas de nitruro de titanio que mejoran sus características superficiales. Con vistas a la aplicación como biomaterial se ha estudiado el incremento de dureza, la resistencia al desgaste y la adherencia de dichas capas al substrato. Se ha diseñado un sistema de medida de la adherencia de la capa nitrurada al metal base mediante flexión controlada en puente de carga. La caracterización de los constituyentes de las capas obtenidas se ha realizado mediante difracción de rayos X, metalografía óptica y SEM. Se ha logrado obtener unas capas de nitruro de titanio con durezas superiores a los 700 Vickers, que confieren al material una buena resistencia al desgaste. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|