Electrostatic Separation of PET/PVC Mixture

Autor: Gordan Bedeković, Branko Salopek, Ivan Sobota
Jazyk: angličtina
Rok vydání: 2011
Předmět:
Zdroj: Tehnički vjesnik
Volume 18
Issue 2
ISSN: 1330-3651
1848-6339
Popis: U današnje vrijeme plastika zamjenjuje druge materijale u mnogim industrijskim granama, pogotovo u proizvodnji ambalaže, zbog čega je i količina otpadne plastike u stalnom porastu. Otpadna plastika može se reciklirati čime se smanjuje prostor potreban za odlagalište i potencijalno štetan utjecaj na okoliš, te ujedno štede prirodni resursi. U radu su prikazani rezultati ispitivanja mogućnosti separacije PET/PVC smjese u elektrostatičkom separatoru. Utjecaj napona elektrode i brzine vrtnje bubnja na učinak separacije ispitivan je na uzorcima različitih klasa veličine zrna (4/3,15 mm, 3,15/2 mm and 2/1 mm). Kao pokazatelji učinkovitosti separacije dvokomponente smjese utvrđivani su kvaliteta koncentrata i iskorištenje korisne komponente. Najbolji rezultati (kvaliteta koncentrata 100 % i iskorištenje 87 %) postignuti su separiranjem klase 4/3,15 mm nakon dva radna stupnja separacije pri naponu elektrode od 15,5 kV i brzini bubnja od 35 m/min.
Nowadays, due to their numerous favorable properties, plastic materials replace other materials in many industries, especially packaging industry, therefore the generation of plastic waste is constantly increasing. Waste plastics can be recycled, which decreases potential harmful influence on the environment and saves landfill space and natural resources. The aim of the research presented in this paper was to evaluate the performance of the electrostatic separator when separating a PET/PVC mixture. The effect of electrode potential and rotor speed on separation efficiency was studied on three different particle size classes (4/3,15 mm, 3,15/2 mm and 2/1 mm). Indicators of separation efficiency for two-component plastic mixture were the concentrate grade and recovery. The best result (100 % grade and 87 % recovery) was obtained by separating coarse particle size class 4/3,15 mm after two separation stages at the electrode potential of 15,5 kV and rotor speed of 35 m/min.
Databáze: OpenAIRE
Externí odkaz: