Оптичні властивості плівок сульфіду кадмію, отриманих методом гарячої стінки
| Autor: | Khrypunov, G. S., Kudiy, D. A., Klyui, N. I., Avksentyeva, L. V., Klyui, A. N. |
|---|---|
| Jazyk: | ukrajinština |
| Rok vydání: | 2022 |
| Zdroj: | Ukrainian Journal of Physics; Vol. 56 No. 4 (2011); 371 Український фізичний журнал; Том 56 № 4 (2011); 371 Scopus-Elsevier |
| ISSN: | 2071-0194 2071-0186 |
| DOI: | 10.15407/ujpe56.4 |
| Popis: | The structure of CdS films deposited with the use of the hot-wall technique has been studied. The growth of a film thickness was found to result in a reduction of mechanical stresses in the films, with compressive and tensile macrostresses being observed in thin and thick films, respectively. The increase of a CdS film thickness was found to be accompanied by an increase in the energy gap width Eg, which is associated with an extension of the coherent scattering region. It is established that CdS films about 0.3 μm in thickness annealed in air are expedient to be used as wide-gap "windows", while fabricating the efficient solar cells based on CdS/CdTe heterosystems. Досліджено структуру плівок сульфіду кадмію, отриманих методом гарячої стінки. Встановлено, що зі збільшенням товщини шарів зменшуються механічні напруження, при цьому при малих товщинах плівки спостерігаються стискаючі макронапруження, а при більших товщинах – розтягуючі. При збільшенні товщини плівки CdS збільшується ширина забороненої зони (Eg), що зумовлено збільшенням розміру областей когерентного розсіювання. Встановлено, що у ролі широкозонних "вікон" для створення ефективних сонячних елементів на основі гетеросистеми CdS/CdTe доцільно використовувати відпалені на повітрі плівки CdS товщиною близько 0,3 мкм. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|