Zaštita od korozije polimernim prevlakama
| Autor: | Meštrović, Lovro |
|---|---|
| Přispěvatelé: | Šimunović, Vinko |
| Jazyk: | chorvatština |
| Rok vydání: | 2022 |
| Předmět: |
korozija
coating testing corrosion TEHNIČKE ZNANOSTI. Strojarstvo. Opće strojarstvo (konstrukcije) korozija metoda pripreme plastificiranje ispitivanja prevlaka method of preparation plastificiranje plasticization TECHNICAL SCIENCES. Mechanical Engineering. General Mechanical Engineering (Construction) metoda pripreme ispitivanja prevlaka |
| Popis: | Korozija ili oksidacija je nezaustavljiv, spontan proces razgradnje materijala koja uzrokuje velike materijalne i financijske posljedice. U cilju spriječavanja razvoja korozije i šteta koje prouzročuje, velika se količina materijalnih sredstava i znanja ulaže u proučavanje nastanka i sprečavanja iste. Ovisno o mjestu i uvjetima eksploatacije razvile su se razne metode zaštite od korozije koje zahtjevaju različite načine nanošenja kao i metode pripreme pred nanošenje. U eksperimentalnom dijelu završnog rada izrađeni su uzorci od aluminijske legure tipa 5086, te su pripremljeni s pet različitih metoda pripreme prije nanošenja antikorozijske prevlake metodom elektrostatskog naprašivanja. U svrhu ispitivanja kvalitete i svojstava prevlake, uzorci su bili podvrgnuti ubrzanim korozijskim ispitivanjima u slanoj i vlažnoj komori koje reprezentiraju višestruko duža vremena eksploatacije no što je vrijeme ispitivanja u komorama. Prije ispitivanja u komorama kao i poslije, ispitana je prionljivost prevlake te otpornost iste na udarna opterećenja. Rezultati ispitivanja su analizirani te su izvedeni zaključci. Corrosion or oxidation is an unstoppable, spontaneous process of material decomposition which causes major material and financial consequences. In order to prevent the development of corrosion, and the damage it causes, a large amount of material resources and knowledge is invested in the study of its origin and prevention. Depending on the place and conditions of exploitation, various methods of corrosion protection, which require different methods of application as well as methods of preparation before application, have been developed. In research that was conducted, samples were made of aluminum alloy type 5086, and prepared with five different methods of preparation before applying the anti-corrosion coating by the method of electrostatic spraying. In order to test the quality and properties of the applied coatings, the samples were exposed to accelerated corrosion tests in salt and wet chambers, which represent many times longer service life than time exposed in the chambers. Before and after testing in the chambers, adhesion of the coating and the resistance of the coating to impact loads was tested. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|