Polianilin İle Fonksiyonelleştirilmiş Karbon Nanotüp/PDMS Nanokompozitlerin Dielektrik Özellikleri
| Autor: | ÜNSAL, Ömer Faruk, ALTIN, Yasin, BEDELOĞLU, Ayşe |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2020 |
| Předmět: |
Karbon nanotüp (KNT)
polianilin (pani) polimer nanokompozit Polymer Science carbon nanotubes (cnts) lcsh:Technology i̇letken polimer dielektrik Nanobilim ve Nanoteknoloji conductive polymer polyaniline (pani) Malzeme Bilimleri Kompozitler karbon nanotüp (cnts) dielectric lcsh:T Carbon Nanotubes (CNTs) Conductive Polymer Dielectric Polyaniline (PANI) Polymer Nanocomposite poly(dimethyl siloxane) (PDMS) Nanoscience and Nanotechnology polymer nanocomposite lcsh:TA1-2040 Materials Science Composites Polimer Bilimi Karbon Nanotüp (CNTs) İletken Polimer Dielektrik Polianilin (PANI) Polimer Nanokompozit Poli (dimetil siloksan) (PDMS) poly(dimethyl siloxane) (pdms) poli (dimetil siloksan) (pdms) lcsh:Engineering (General). Civil engineering (General) Poly (dimethyl siloxane) (PDMS) Letken polimer |
| Zdroj: | Uludağ University Journal of The Faculty of Engineering, Vol 25, Iss 2, Pp 861-874 (2020) Volume: 25, Issue: 2 861-874 Uludağ Üniversitesi Mühendislik Fakültesi Dergisi |
| ISSN: | 2148-4155 2148-4147 |
| Popis: | In recent years, carbon nanotubes (CNTs) have emerged as materials that are often used in the preparation of polymer nanocomposites with conductive or advanced dielectric properties due to their unique properties including high temperature and electrical conductivity, which allows the production of very light and robust materials with a very high length-to-diameter ratio. However, during the preparation of polymeric nanocomposites with these materials, some problems are encountered. One of the major problems is that after preparing these conductivematerials or adding them into the polymer, they tend to aggregate, forming agglomerate, due to their conductive structures. Therefore, in this study, firstly, multi-walled carbon nanotubes (MWCNTs) were functionalized with conductive form of polyaniline (PANI) and subsequently, the poly (dimethyl siloxane) (PDMS) polymer nanocomposite films with different concentrations of functionalized multi-walled carbon nanotubes were prepared. Then, the structural, morphological, electrical and dielectric properties of the films were characterized. As a result, with the addition of only 1.5% PANI-CNT, the dielectric constant of PDMS was increased by 47-fold at 1 Hz. The dielectric films like presented here can be used in capacitors, flexible electronics, dielectric elastomers and artificial muscle applications. Son yıllarda, yüksek uzunluk/çap oranı ile hafif ve sağlam kompozitler hazırlanmasını mümkün kılan karbon nanotüpler, yüksek ısıl ve elektriksel iletkenlikleri gibi benzersiz özelliklerinden dolayı iletkenlik veya dielektrik özellikleri yüksek polimer nanokompozitlerin üretiminde kullanılan bir malzeme olarak ortaya çıkmıştır. Bununla birlikte, bu malzemelerle polimerik nanokompozitlerin hazırlanması sırasında bazı problemlerle karşılaşılmaktadır. En büyük sorunlardan biri, bu iletken malzemeleri hazırladıktan veya polimere ekledikten sonra, iletken yapılarınedeniyle topaklanma, topak oluşturma eğilimi göstermeleridir. Bu nedenle, bu çalışmada ilk olarak, çok duvarlı karbon nanotüpler (MWCNT'ler) polianilinin iletken formu (PANI) ile fonksiyonelleştirilmiştir. Ardından, farklı konsantrasyonlarda fonksiyonelleştirilmiş çok duvarlı karbon nanotüplere sahip nanokompozit poli(dimetil siloksan) (PDMS) polimer filmler hazırlanmıştır. Daha sonra ise, filmlerin yapısal, morfolojik, elektriksel ve dielektrik özellikleri karakterize edilmiştir. Sonuç olarak, sadece % 1,5 PANI-CNT ilavesiyle, PDMS'nin dielektrik sabiti 1 Hz'de 47 kat arttırılmıştır. Burada ortaya konulduğu gibi dielektrik filmler kapasitörler, esnek elektronik, dielektrik elastomer ve yapay kas uygulamalarında kullanılabilir. |