Production And Characterization Of B4c Based Composites From B4c/me Starting Powders By Using Spark Plasma Sintering (sps) Method

Autor: Cengiz, Meral
Přispěvatelé: Şahin, Filiz, Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı, Malzeme Bilimi ve Mühendisliği, Material Science and Engineering
Jazyk: turečtina
Rok vydání: 2016
Předmět:
Popis: Tez (Doktora) -- İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, 2016
Thesis (PhD) -- İstanbul Technical University, Institute of Science and Technology, 2016
B4C, elmas ve kübik bor nitrürden sonra bilinen en sert malzeme olup, yüksek aşınma direncine, yüksek nörtron absorblama özelliğine, yüksek kimyasal dirence ve düşük yoğunluğa sahiptir. Bu özelliklerinden dolayı B4C seramikleri, havacılık-uzay uygulamalarından, askeri amaçlı zırh sistemleri ve nükleer uygulamalara kadar geniş bir kullanım alanına sahiptir. Kovalent bağlı kristal yapısı, 2450 °C lere varan çok yüksek ergime sıcaklığı ve düşük self difüzivitesi nedeniyle belirtilen üstün özelliklere sahip B4C malzemeler, ancak yüksek sıcaklık ve basınç uygulamaları ile üretilebilmektedir. Yüksek rölatif yoğunluğa sinterlenebildiğinde bile B4C’ün en önemli mekanik zayıflığı kırılma tokluğunun düşük olmasıdır. Bu doktora çalışmasında, savunma sanayine ve nükleer uygulamalara yönelik B4C’ün kırılma tokluğu, yapıya farklı ergime sıcaklığına ve yoğunluklara sahip metalik katkılar ilave edilerek yükseltilmeye çalışılmış, bununla birlikte enerji sanayine yönelik B4C’ün nötron absorpsiyonunun yanında gama ışımalarına karşı radyasyon kalkan özelliğini geliştirip geliştirmediği incelenmiştir. Bu tez çalışması kapsamında bor karbür-metal toz karışımlarından hareketle tek kademeli spark plazma yöntemi ile kompakt yapıların üretilmesi ve proses parametrelerinin optimizasyonu sağlanmış ardından elde edilen veriler yardımıyla ve üretilen seramik ve kompozitler kullanılarak fiziksel, mekanik ve nükleer karakterizasyonları gerçekleştirilmiştir. Bu doktora çalışmasında deneysel çalışmalar kapsamında İstanbul Teknik Universitesi, Metalurji ve Malzeme Mühendisliğinde 2007 yılında kurulumu tamamlanan 20.000 A kapasiteli SPS 7.40 MKVII, SPS Syntex Inc. cihazı kullanılarak 50x50 mm kare kesitli 5 mm kalınlığındaki kompozitlerin üretimi gerçekleştirilmiştir. İlk defa uç ürüne uygun boyutta ve kare geometride üretilmesi sağlanmış bu ürünlerin kenar ve merkez bölgelerinin fiziksel ve mekanik özelliklerinin farklılıkları incelenmiş, numunelerin nötron ve gama ışımalarına tabi tutulması sağlanarak radyasyon kalkan özellikleri belirlenmiştir. Radyasyon ile ilgili test ve karakterizasyonlar, İTÜ Enerji Enstitüsü, Radyasyondan Korunma ve Radyoekoloji Araştırma Grubu tarafından gerçekleştirilmiştir. Farklı bor karbür-metal toz karışımlarından hareketle, üstün özellikli B4C-metal kompozitlerinin kısa süre ve düşük sıcaklık avantajı ile tek kademede üretilmiş, böylece ürünlere mevcuta göre istenmeyen ara fazların minimize edildiği, geliştirilmiş özellikler kazandırılması sağlanmıştır. Bor karbürün, söz konusu metallerle, uygun sıcaklıklarda spark plazma sinterleme sonucu elde edilen ürünlerde hangi fazların oluştuğu X-ışınları difraktometresi yardımı ile belirlenmiştir. Uygun görülen sıcaklıklarda oluşması beklenen fazlar, önce B-C-Me denge diyagramlarında ilave ettiğimiz metal oranına göre hangi faz bölgesinde kalınacağını anlamak için, B, C ve metal içerikleri miktarsal olarak hesaplanarak, oksijen içerikleri belirlenmiş ardından Fact Sage 7 Termo Kimyasal programı ile başlangıç malzemelerinin miktarları da dikkate alınarak, oluşması muhtemel fazlar simüle edilmiştir. Birbirinden farklı ve düşük yoğunluklu, farklı ergime sıcaklığına sahip metal ilaveleri kullanılarak (Al, Si ve Ti), hacimce farklı oranlarda (%5, 10, 15 ve 20) HS kalite H.C. Starck marka B4C tozuna katılarak sıcaklık, uygulanan basınç, ısıtma hızı, sinterleme süresi ve kullanılan atmosfer gibi farklı parametreler kullanılarak üretimler gerçekleşmiştir. Grafit kalıplardan çıkarılan numuneler kumlama ile yüzeyleri temizlendikten sonra, fiziksel, mekanik ve radyasyon karakterizasyon işlemlerine tabi tutulabilmek için uygun boyutlara elmas disk yardımıyla kesilmiştir. Numunelerin yoğunluğu Archimed’s prensibi kullanılarak ölçülmüştür. Numuneler elmas çözeltiler kullanılarak parlatılmış sertlik ve kırılma toklukları indentayasyon tekniği ile ölçülmüştür. Tüm numunelerde faz dönüşümü, X-ışınları difraktometresi ile takip edilmiştir. Mikro yapı çalışmalarında alan emisyonlu taramalı elektron mikroskobu kullanılmıştır. B4C- Al kompozitleri için çeşitli deneylerde sıcaklık 1370 ile 1450 °C arasında değiştirilirken, spark plazma sinterleme süresi, 0, 2, 4 ve 8 dak. olarak ve ısıtma hızları ise 100 ve 200 °C/dak. olarak denenmiştir. B4C-%5 Al karışımlarının 100 °C/dak. ıstma hızı, 1450 °C, 4 dak. süreyle 40 MPa basınç uygulanarak gerçekleştirilen SPS deneylerinde rölatif yoğunluk %100’e yükselirken, numunelerde 29,7 GPa sertlik ve 3,36 MPa.m1/2 kırılma tokluğu değerleri elde edilmiştir. 100 °C/dak. ısıtma hızı, 1410 °C SPS sıcaklığı, 4 dak. SPS süresi ve 40 MPa basınç uygulanarak üretilen % 10, % 15 ve % 20 Al içeren numunelerin rölatif yoğunluk değerleri % 97,9, % 97,9 ve % 98,3 olarak ölçülmüş olup, artan Al içeriği ile sertlik değeri 29,6 GPa’dan 28,9 GPa’a değişmiştir. Kırılma tokluğu değeri ise 4,45 MPa.m1/2 değerine ulaşmıştır. B4C- hac. %5 Si kompozitleri için çeşitli deneylerde sıcaklık 1300 °C, 1400 °C ve 1500 °C olarak değiştirilirken, spark plazma sinterleme süresi, 0 ve 4 dakika olarak ve uygulanan basınç 40 ve 60 MPa olarak değiştirilmiştir. Başlangıç tozlarındaki Si içeriği %10, %15 ve %20’ye yükseltilerek deneyler 1500 °C’de 40 MPa’da yapılmış; %15 Si ve %20 Si içeren numuneler ergiyerek kalıba yapıştığından, sıcaklık %15 ve %20 Si içeren numuneler için 1450 °C’a düşürülmüştür. Artan Si içeriği ile merkez-kenar arasındaki yoğunluk farkları azalmış, yoğunluk değerleri yükselmiştir. Sertlik değerleri yüksek yoğunluğun elde edildiği merkez bölgelerde 28 GPa’a kadar yükselirken kenar bölgelerde en yüksek sertlik 22 GPa olarak ölçülmüştür. Kırılma tokluğu 3,42-3,32 MPa.m1/2 aralığında değişmiştir. B4C-Ti kompozitlerinde; hacimce %5 Ti içeren numunelerde rölatif yoğunluk değerleri 1450 °C’de % 83,1 iken hac. %20’ye kadar artan Ti ilavelerinde bu değer %98,6’ya yükselmektedir. Ti miktarının yoğunluk üzerindeki etkisine benzer olarak, B4C-Ti kompozitlerinin rölatif yoğunlukları spark plazma sinterleme sıcaklığının yükseltilmesiyle artış göstermektedir. Merkez ve kenar bölgeler arasındaki rölatif yoğunluk farkının azalması sonucu artan sıcaklığın ve Ti miktarının homojenizasyona olumlu etkide bulunduğu belirlenmiştir. Ti metalinin ergime sıcaklığı bor karbür ana matris fazının ergime sıcaklığından daha düşük olduğundan spark plazma sinterleme sırasında, Ti, bor karbür taneleri arasındaki boşluklarda, ergiyerek sıvı faza geçmekte, B4C ile reaksiyona girmekte ve yapısına B’u alarak, TiB2 oluşturmaktadır. Artan Ti miktarlarına bağlı olarak sertlik değerleri %5 Ti içeren numunelerde 29,68 GPa’dan %20 Ti içeren numunelerde 25,32 GPa’a düşmüştür. TiB2’ün sertliği (24-29 GPa), B4C’ün sertliğinden (32-36 GPa) daha düşük olduğundan yapıdaki TiB2 miktarının artması kompozitin sertliğinin azalmasına neden olmuştur. B4C -TiB2 kompozit numunelerine Ti ilavesi arttıkça yapıda oluşan TiB2 miktarı yükselmekte, kırılma tokluğu değeri de artış göstermektedir. 1550 °C’da artan Ti katkısı ile kırılma tokluğu değeri 5,4 MPa.m1/2 değerine kadar artarken, en yüksek kırılma tokluğu değeri 1500 °C’da sinterlenmiş % 20 Ti katkılı numunede 5,9 MPa.m1/2 olarak ölçülmüştür. Kırılma tokluğundaki bu artış, yapıda oluşan TiB2’nin ana matris olan B4C’den farklı termal genleşme katsayısına sahip olması ve soğuma sırasında termal genleşme farklılıklarının sebep olduğu gerilmeler, mikro çatlaklar, TiB2 tanelerinin çatlak yönünü değiştirmesi ve çatlağın enerjisini absorblaması şeklinde açıklanabilmektedir. B4C-Ti, B4C-Si ve B4C-Al kompozitlerinin gama radyasyonu zırhlama özellikleri incelendiğinde bor karbür içerisine titanyum, silisyum ve aluminyum katkılarının yapılması ile malzemelerin yoğunluk değerlerinde artış görülmüştür. Bu artışa bağlı olarak Cs-137 gibi Co-60 gama radyasyonu içinde katkılarının yapılması ile saf bor karbüre oranla daha düşük kalınlık ve hacimli bir zırhlama imkânı ortaya çıkmaktadır. B4C-Ti, B4C-Si ve B4C-Al kompozit malzemelerinin, termal nötronlar karşısındaki YDK değerleri incelendiğinde saf B4C için 0,973 cm olan değerin, hac. %20 Ti katkılı numuneler için 1,674 cm, % 20 Si katkılı numunelerde 1,953 cm ve %20 Al katkılı kompozitte 1,868 cm değerine kadar yükseldiği görülmektedir. Ti atomunun ağırlığının Al ve Si atomlarına göre yüksek değerde olması sebebiyle ortamdaki elektron yoğunluğunun en yüksek değerinin titanyum katkısı ile sağlanması gama radyasyonu karşısında Ti katkılı malzemelerin daha yüksek zırhlama kabiliyetine sahip olmasının nedeni olarak belirlenmiştir. Gama radyasyonunun aksine, termal nötronlar için bor karbür malzeme içerisine titanyum, silisyum ve aluminyum katkılarının yapılması malzeme içindeki mevcut B4C oranını ve bağlantılı olarak Bor-10 izotopu oranını düşürmekte olduğundan daha düşük radyasyon zırhlama özelliği göstererek YDK değerlerini arttırmaktadır. Her üç metalik katkı malzemesi, radyasyon zırhlama açısından kıyaslandığında, atom ağırlığı yüksek olan titanyumun, gama ve nötron zırhlamasında Al ve Si metallerine göre daha etkin bir gama zırhlaması sağlarken, nötron zırhlamasındaki negatif etkisinin diğer iki metalden daha düşük olduğu görülmektedir.
B4C exhibits high wear resistance, high chemical resistance and high neutron absorption capacity and having low density and known to be the third hardest material after diamond and cubic boron nitride. Having superior properties B4C ceramics exhibit a great range of application areas from aeronautic-space applications to ballistic and nuclear applications. Due to its covalently bonded crystal structure of reaching up to 2450 °C melting temperature and low self-diffusivity, B4C materials with superior properties mentioned above can only be produced by high temperature and pressure applied techniques. The most important mechanical weakness of B4C even if it is sintered to high relative densities is its low fracture toughness. In many reseaches it is emphasised that the disadvantages of B4C can be overcomed by either adding a new secondary phase or nano particles. In this study, as for the defense industry structure, fracture toughness of B4C is tried to be increased by metallic additives having different melting temperatures; moreover, for the energy industry gamma radiation resistance and neutron absorbtion capability of B4C is tried to be increased further. Spark plasma sintering, as a relatively new method is used for sintering B4C specimens in this study. SPS method have many advantages over other traditional and currently widespread other sintering methods. These advantages may be expressed as; very fast sintering rate, lower sintering temperatures and less energy consumption leading to prevention of grain coarsening, and increasing the physical and mechanical properties of the materials. Typically, ceramic-metal composites containing high amount of ceramic, are initially obtained by pressureless sintering methods to obtain porous ceramic and porous metal structures and futher produced by infiltrating the metal at a temperature above the metals melting temperature. However, lack of a homogeneous porous structure, wetting difficulties encountered in the structure of B4C results in long and non- homogeneous infiltration which becomes the most important disadvantage of this process. Spark Plasma Sintering of this study on the basis of a new production technique, different boron carbide-metal powder mixtures, high-specification B4C-metal composites with the short-process duration and low-temperature advantage of single-stage production is used in order to minimize intermediate phases and unwanted by products that would cause the fracture toughness to decrease. The original aspects of this study is to have a systematical investigation of the effect of metal additions (Al, Si and Ti) having low density and different melting temperatures on spark plasma sintering parameters and material characteristics of the produced materials, and investigate and compare the possible phases that might occur during spark plasma sintering throughout the experiments and to make their thermodynamic evaluation by Fact Sage software and to compare the experimental data with B4C-metal containing structures in the end product. In the SPS experiments, phases expected to occur in different temperatures are determined by Fact Sage software and compared with the XRD analysis results and further analysis is made regarding the status of the system's thermodynamic sintering temperature. In addition, the correct size and square geometry appropriate to the end products will be achieved for the first time. Starting from the physical and chemical characterization of powders, powder mixtures of B4C-metal in appropriate compositions are weighed and mixed in ball milling with sufficient Merck quality ethanol. After granulating, dried powders are loaded into the square graphite molds and is spark plasma sintered at various temperatures, pressures and soaking times. Samples were produced by SPS apparatus with 20000 A capacity SPS 7.40 MKVII, SPS Syntex Inc. instrument established in Chemical and Metallurgical Engineering Faculty/Materials and Metallurgical Engineering Department of Istanbul Technical University. After cleaning the surfaces of the samples extracted from the graphite moulds by sand blasting; for physical, mechanical and nuclear characterization they are cut by diamond wheel in order to achieve appropriate dimensions for characterization. The density of the samples are measured by using Archimedes' principle. Hardness and fracture toughness values of the samples are measured by indentation method, after polishing the sample pieces using diamond suspensions down to 1µm. All phase transformations of the samples are investigated by X-ray diffractometer. Field emmisive scanning electron microscopy (FE-SEM) is used for microstructure analysis. B4C-Al, B4C-Si and B4C-Ti composite materials produced by spark plasma sintering system is subjected to neutron and gamma radiation in order to determine their shielding properties. Radiation testing and characterization of monolithic B4C samples, B4C-Al, B4C-Si and B4C-Ti samples are carried out by Istanbul Technical University, Institute of Energy, Radiation Protection and Radioecology Research Group. For B4C- Al composites various temperature values between 1370-1450 °C and spark plasma sintering time as 0, 2, 4 and 8 min. are chosen whereas the heating rate is selected to be 100 and 200 °C/min. The relative density values reached upto 100% for B4C-vol.5% Al mixture spark plasma sintered at 1450 °C for 4 min. with a heating rate of 100 °C/min. under 40 MPa applied pressure. When microstructures of the spark plasma sintered B4C-5%Al composites are investigated, it is observed that low SPS temperetures and short sintering durations would cause the structure to stay porous whereas at 1450 °C the microstructures observed to have no pore at all. Hardness and fracture toughness of the mentioned samples are measured to be 29.7 GPa and 3.36 MPa.m1/2 respectively. During spark plasma sintering, there are local smelting within the sample as Al content increases, therfore, sintering temperatures are decreased to 1410 °C. Relative density values are measured to be 97.9%, 97.9%, and 98.3% for the 10%, 15% and 20%Al including B4C samples spark plasma sintered with a heating rate of 100 °C/min., at 1410 °C SPS temperature, for 4 min. soaking time under 40 MPa applied pressure. As Al content increased the hardness values varied between 29.6 GPa to 28.9 GPa and fracture toughness values reached to values up to 4.45 MPa.m1/2. The decrease in hardness values are caused due to the increased amount of AlB12 and graphite phases occurred from the reaction of B4C with Al. For B4C-Si composites as the spark plasma sintering temperature increases, liquidified Si, taking C from graphite dies, B4C and using excess C, forms SiC. Various spark plasma sintering temperatures such as 1300 , 1400 and 1500 °C for B4C-%5 Si composites; 0 and 4 minutes soaking times and 40 and 60 MPa applied pressure is used. Si content is increased to 10%, 15% and 20% in vol. for the starting powder at 1500 °C under 40 MPa and decreased to 1450 °C since for the 15% and 20% Si containing composites the samples are smelted and sticked to the inner surfaces of the moulds. As the Si amount increased, edge-center relative density differences are decreased and the density values are increased itself. Hardness values are obtained to be up to 28 GPa at the centers that high relative densities are obtained to be 22 GPa for edges. Fracture toughness values varied from 3,42 to 3,32 MPa.m1/2. As the Si amount increases in the composites SiC is formed in the final structure in the grain boundaries. As cracks reach the B4C-SiC interface, they do not extend along the interface but cross B4C-SiC particles since fracture toughness of SiC is higher that B4C. The toughness of the composite is higher than that of single B4C because the transgranular cracks formation can consume more energy. Relative density values in samples with 5% Ti by volume, spark plasma sintered at 1450 °C increased from 83.1% up to 98,6 % when the Ti amount increased to 20%. Similar to the effect of Ti amount on relative density, temperature increase acts for the favor of relative density as well. Increasing temperature and Ti amount in B4C composites leads to homogenity. During spark plasma sintering, since the melting temperature of Ti is much less than the melting tempereture of B4C as the main matrix, Ti metal starts to melt and fill the voids between B4C grains and melt while transfering to the liquid phase and reacts with B4C and takes B to its structure to constitude TiB2 phase. Since the B4C phases gets poorer on behalf of B as the B from B4C phase reacts with Ti to form TiB2; graphite phase is envealed. This newly formed TiB2 grains, due to Ti getting into liquid phase and new grains are nucleated on the surface of B4C grains, they take B4C phases as the main phases and form as large TiB2 grains as B4C matrix grains. This process further goes on until all of the coarser Ti grains are melted and transformed into finer TiB2 grains. In the middle of this newly formed TiB2 agglomerated grains there occurs graphite phase as lamel like structure. When B4C-Ti micrographs obtained from the fructure surfaces are observed B4C grains are bonded strongly with spark plasma sintering as a result, the crack passes through the B4C grains (transgrannular) and when it reaches to TiB2 grains (TiB2 agglomerate grain group) the crack passes along the weakly bonded TiB2 grain boundaries (intergrannular). Depending on the increasing Ti content from 5% Ti to 20% Ti, hardness decreased from 29.68 down to 25.32 GPa. As the TiB2 amount increases in the structure, since the hardness of TiB2 (24-29 GPa), is much lower than the hardness of B4C (32-36 GPa), the total hardness of the composite show a tendency to decrease. In the B4C-TiB2 composite samples, as Ti amount increases TiB2 amount increases in the bulk material as well leading to an increase in the fracture toughness values. The fracture toughness value increases to 5.4 MPa.m1/2 at 1550 °C and the highest fracture toughness value reached is 5.9 MPa.m1/2 for the 20% Ti included samples at 1500 °C. This increase in fracture toughness, is caused by the main matrix B4C having a different thermal expansion coefficient than newly formed TiB2 and stress caused by thermal expansion differences during the cooling phase leads to micro cracks and furthermore changes the direction of cracks and thus absorb the energy of the crack during long path way. When gamma radiation shielding properties are investigated B4C-Ti, B4C-Si and B4C-Al composites, titanium, silicon and aluminum addition into boron carbide lead to an increase in the density of the materials. Due to that sort of increase, against Cs-137 Co-60 gamma radiation there arises a better shielding opportunity with a lower thickness and volume compared to monolithic boron carbide. When the HVT (Half Value Thickness) values are investigated against thermal neutrons, for the B4C-Ti, B4C-Si and B4C-Al composites, for monolithic boron carbide it is measured as 0.973 cm; for the 20%Ti included composites it is measured as 1.674 cm, for the 20%Si included composites it is measured as 1.953 cm and for the 20% Al included composite it is measured as 1.868 cm. Since the molar mass of Ti atoms are greater than Si and Al atoms, electron density is higher in the environment due to the high electron number of Ti and as a result Ti contributes more to the gamma shielding properties of the composites. In contrast to gamma radiation shielding, the titanium, silicon or aluminum addition into boron carbide composite would increase the HVT values against thermal neutrons in other words metal additions would decrease the shielding capacity since increasing the metal content would decrease the ratio of B4C in the bulk structure causes a reduction in the boron-10 isotope ratio accordingly. When the three metal additives are compared within each other about their gamma shielding properties, Ti having a higher atomic number seems to be a more efficient additive, and the negative effect that it possesses on the material against neutron shielding is less than others are. In this study, spreading the application areas of boron products such as B4C-Al, B4C-Si and B4C-Ti composites exhibiting superior properties as well as the cost-effective production and use of new production technologies of new boron products have been the main goal. Physical, mechanical and radiation shielding properties of monolithic boron carbide has been improved in order to overcome many disadvantages due to production or content of the boron carbide ceramics. Thus ‘Investigation of Boron products with the use of a variety of products that might create a synergy effect will allow the widespread use of national resources effectively and in the future will be used as a reference for the development of alternative studies. In such studies carried out with B4C-metal composite system in terms of nuclear radiation shielding, the use of boron-containing products will be promoted by the National sources.
Doktora
PhD