| Autor: |
Ramshorst, M.C.J. van, Benedetto, G.L. di, Duvalois, W., Hooijmeijer, P.A., Heijden, A.E.D.M. van der |
| Jazyk: |
angličtina |
| Rok vydání: |
2016 |
| Předmět: |
|
| Zdroj: |
Propellants, Explosives, Pyrotechnics, August, 4, 41, 2632-2642 |
| Popis: |
The failure mechanism of a propellant consisting of hydroxyl terminated poly-butadiene filled with ammonium perchlorate and aluminum (HTPB/AP/Al) was determined by performing in-situ uniaxial tensile tests in a scanning electron microscope (SEM). The experimental test plan contained uniaxial tensile test experiments performed at room temperature (25 °C) at three different strain rates (30, 150 and 750 μm min−1). The in-situ images and in-situ videos collected by the SEM were correlated with the stress-strain diagrams created with the tensile experiments, in order to relate the failure mechanism to the features found in the stress-strain diagram. No significant strain rate dependency of the failure mechanism was observed when working with strain rates up to 750 μm min−1 and working at room temperature. The stress-strain diagram showed indications of existing cracks and voids opening up prior to the creation of new cracks and/or voids in the sample, debonding of binder with AP particles as well as nucleation and coalescence of voids. On the fracture surfaces of the samples, it was apparent that the binder cleanly separated from the large AP particles but had a better bond with the aluminum particles. However, a difference in the appearance of a short drawing phase in the stress-strain diagram of the propellant is observed at different strain rates. The presented results clearly demonstrate the major advantage of the combination of microscopic tensile tests with microscopic observations, linking the stress-strain behavior to the mechanical deformation processes taking place in these propellant samples at the microscopic level. |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|