The Li+, Na+ and K+ ion exchange reaction process on the surface of mixed oxide SiO2/TiO2/Sb2O5 surface prepared by the sol-gel processing method
| Autor: | Ferreira, C. U., Gonçalves, J. E., Kholin, Y. V., Gushikem, Y. |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2005 |
| Předmět: | |
| Zdroj: | Eclética Química v.30 n.1 2005 Eclética Química Universidade Estadual Paulista Júlio de Mesquita Filho (UNESP) instacron:UNESP Eclética Química, Volume: 30, Issue: 1, Pages: 51-58, Published: 2005 |
| Popis: | The porous mixed oxide SiO2/TiO2/Sb2O5 obtained by the sol-gel processing method presented a good ion exchange property and a high exchange capacity towards the Li+, Na+ and K+ ions. In the H+/M+ ion exchange process, the H+ / Na+ could be described as presenting an ideal character. The ion exchange equilibria of Li+ and K+ were quantitatively described with the help of the model of fixed tetradentate centers. The results of simulation evidence that for the H+ / Li+ exchange the usual situation takes place: the affinity of the material to the Li+ ions is decreased with increasing the degree of ion exchange. On the contrary, for K+ the effects of positive cooperativity, that facilitate the H+ / K+ exchange, were revealed. O óxido misto poroso SiO2/TiO2/Sb2O5, obtido pelo método de processamento sol-gel, apresentou uma boa propriedade e elevada capacidade de troca iônica com os íons Li+, Na+ e K+. No processo de troca iônica H+/M+, o H+/Na+ apresentou um caráter ideal. Os equilíbrios de troca de Li+ e K+ foram quantitativamente descritos através de um modelo de centros tetradentados fixos. Os resultados de simulação evidenciaram que para troca H+/Li+ temos uma situação normal: a afinidade do material pelo íon Li+ decresce com o aumento do grau de troca. Para o K+, o efeito positivo do cooperativismo que facilitaria a troca H+/K+, revelou um efeito contrário. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|