Diffusion and Defect Data Part A: Defect and Diffusion Forum; December 2023, Vol. 429 Issue: 1 p209-218, 10p |
| Abstrakt: |
To understand the nano phase formation, cooling experiments of a hypereutectic Zn-Al alloy containing 6 wt% of Al are carried out under two different cooling rates of 0.04 and 10.00 °C/s. The applied cooling rates significantly influence the phase change behavior of the investigated alloy. The liquidus temperature (TN) for the nucleation of the primary phase decreases from 390.3 to 382.9 °C, and the undercooling increases from 0.7 to 8.1 °C, as the cooling rate rises from 0.04 to 10 °C/s. The eutectic and eutectoid temperatures decrease from 381.5, 277.7 to 375.6 and 267.6 °C, respectively, when the cooling rate increases from 0.04 to 10.00 °C/s. The SEM and EDS analyses reveal that the solidified alloy contains the primary γ-ZnAl phase, the eutectic β-Zn phase, and the eutectoid α-Al and eutectoid β-Zn phases. The fast phase change and transformation caused by rapid cooling results in the formation of nano eutectoid phases and fine microstructure. |
| Databáze: |
Supplemental Index |
| Externí odkaz: |
|