Sivakesavam, O., Prasad, Y. V. R. K. |
| Zdroj: |
International Journal of Materials Research: Zeitschrift fuer Metallkunde; February 2022, Vol. 94 Issue: 11 p1255-1259, 5p |
| Abstrakt: |
Processing maps have been developed for hot deformation of Mg–2Zn– 1Mn alloy in as-cast condition and after homogenization with a view to evaluate the influence of homogenization. Hot compression data in the temperature range 300 – 500 °C and strain rate range 0.001 – 100 s– 1were used for generating the processing map. In the map for the as-cast alloy the domain of dynamic recrystallization occurring at 450 °C and 0.1 s–1has merged with another domain occurring at 500 °C and 0.001 s– 1representing grain boundary cracking. The latter domain is eliminated by homogenization and the dynamic recrystallization domain expanded with a higher peak efficiency occurring at 500 °C and 0.05 s–1. The flow localization occurring at strain rates higher than 5 s–1is unaffected by homogenization. |