Electrical Conductivity and Phase Transitions in Ferroelectric Solid Solutions Li0.17Na0.83ТауNb1-уO3 (y = 0 – 0.5) in High Pressure

Autor: Efremov, Vadim V., Palatnikov, Mikhail N., Radyush, Yuriy V., Shcherbina, Olga B.
Zdroj: Diffusion and Defect Data Part B: Solid State Phenomena; September 2020, Vol. 310 Issue: 1 p6-13, 8p
Abstrakt: Ferroelectric ceramic solid solutions LixNa1-xTayNb1-yO3 (х = 0.17; у = 0 – 0.5) with the perovskite structure have been obtained by the thermobaric synthesis method. Particularities of their microstructure, elastic properties, electrical conductivity and permittivity have been researched. It has been established that an increase in the thermobaric synthesis temperature leads to a decrease in the Young’s modulus value. Specific static conductivity values have been determined; charge carrier activation enthalpies На have been calculated. The Curie temperature of the samples has been determined to decrease with an increase in tantalum content. A Ferroelectric ceramic solid solution Li0.17Na0.83Ta0.1Nb0.9O3 was shown to undergo four structure phase transitions in the temperature range 300-820 К. A Li0.17Na0.83Ta0.1Nb0.9O3 has been shown to be a high temperature superionic. Possible mechanisms of the detected phenomena are discussed.
Databáze: Supplemental Index