| Abstrakt: |
Experimental studies of bending deformation of carbon - and fiberglass samples after 8-month exposure in full-scale conditions were performed and the modulus of transverse elasticity was determined. It was found that the influence of the external environment on fiberglass samples is more significant. For carbon fiber, there was an average decrease of 7.1%, and for fiberglass-by 14%. Modification of samples in ultrahigh frequencies (UHF) electromagnetic field reduces the negative influence of the environment: the values of the transverse elastic modulus of carbon fiber and fiberglass samples are reduced by 5% and 11%, respectively. It is shown that the UHF electromagnetic field in rational modes can increase the modulus of transverse elasticity of carbon fiber by (27-30)%, fiberglass – by (20.8-25.6)% with a significant increase in the uniformity of this parameter. Experimental studies of the bending deformation of carbon-and fiberglass specimens after 8-month exposure in natural conditions have been carried out, and the shear elastic modulus has been determined. It has been established that the influence of the external environment on fiberglass samples is more significant. For carbon fiber reinforced plastic, a decrease was noted on average by 7.1%, for fiberglass - by 14%. Modification of samples in a microwave electromagnetic field helps to reduce the negative influence of the external environment: the values of the shear modulus of the prototypes of carbon fiber reinforced plastic and fiberglass are reduced by 5% and 11%, respectively. It is shown that the microwave electromagnetic field in rational modes allows increasing the transverse elastic modulus of carbon fiber reinforced plastic by (27-30)%, fiberglass - by (20.8-25.6)% with a significant increase in the uniformity of this parameter. |