de Diego Calderon, Irene, Salib, Matthieu, Kabou, Nora, Arlazarov, Artem |
| Zdroj: |
Materials Science Forum; December 2018, Vol. 941 Issue: 1 p530-535, 6p |
| Abstrakt: |
A steel containing Fe-0.2C-2Mn-Si-Al was annealed using intercritical Q&P cycles. Quenching temperature and partitioning time at 440°C was varied. Analysis of microstructure evolution during such Q&P treatments was performed using different characterization tools: FEG-SEM, EBSD, dilatometer and saturation magnetization measurements. Especially, phenomena taking place during partitioning were investigated. The microstructure was analyzed at the end of soaking, before and after partitioning and at the end of the annealing cycle. It was found that bainite transformation happens during partitioning and has a significant effect on the final retained austenite fraction. Quenching temperature has an important effect on both martensitic transformation during cooling and subsequent bainite transformation during partitioning. |
| Databáze: |
Supplemental Index |
| Externí odkaz: |
|