Materials Science Foundations; March 2015, Vol. 81 Issue: 1 p429-456, 28p |
| Abstrakt: |
The chapter is devoted to a study of the influence of neutron irradiation on the martensitic transformations and shape memory effects in TiNi-based shape memory alloys. Irradiation of the samples was carried out in the low-temperature helium loop of a WWR-M fusion reactor at Petersburg Nuclear Physics Institute in Gatchina (Russia). The experimental data showed that the variation in transformation temperatures depended on the irradiation temperature. The main factors influencing the variation in transformation temperatures during irradiation were disordering of the solid solution at low temperatures, radiation ordering at high temperatures, and thermally activated annealing of radiation damage. All of these mechanisms were taken into account in the differential equation given in the present work for description of the transformation temperature variation during irradiation at different temperatures. It was found that irradiation up to a fluence of 7·1018 cm-2 did not suppress the transformation plasticity and shape memory effects in TiNi alloy in spite of the variation in transformation temperatures. It was observed that the shape memory effect may be initiated by irradiation up to a fluence of 5·1020 cm-2 at a constant temperature (under isothermal conditions) due to a decrease in transformation temperatures. |
| Databáze: |
Supplemental Index |
| Externí odkaz: |
|