IOP Conference Series: Materials Science and Engineering; March 2018, Vol. 317 Issue: 1 p012073-012073, 1p |
| Abstrakt: |
Stress corrosion cracking (SCC) behavior of the hardening-treated materials of 13Cr stainless steel was examined with SSRT tests and constant load tests. In the simulated geothermal water and even in the test water without addition of impurities, the hardening-treated materials showed a brittle intergranular fracture due to the sensitization, which was caused by the present hardening-treatments. |