| Autor: |
Buggakupta, Wantanee, Chuankrerkkul, Nutthita, Surawattana, Juthathep |
| Zdroj: |
Key Engineering Materials; August 2015, Vol. 659 Issue: 1 p90-95, 6p |
| Abstrakt: |
This work focuses on the debinding conditions of the ceramic materials fabricated by powder injection moulding. Ceramic powder materials, including alumina and alumina-based composites were prepared as feedstocks and mixed with water-soluble polyethylene glycol (PEG) and polyvinyl butyral (PVB). The PEG/PVB binder mixture, with PEG to PVB ratio of 85:15 by weight and powder loading of 44 vol%, were thoroughly mixed and injected into the mould at the temperature of 190 °C to obtain rod-like specimens. Prior to sintering, the as-injected specimen was then leached in water, the temperature of which was varying from 30 (ambient temperature), 45 to 60 °C, in order to get rid of PEG and leave the specimens in shape by PVB. The rate of PEG removal according to different water temperatures was investigated. The experimental results suggested that PEG could completely be eliminated by 45 and 60 °C water without any dimensional disintegration in 5 hours whereas those leached in 30 °C water showed only 70% PEG removal. Higher water temperatures led to fast PEG removal rate at the beginning and then gradually decreased with elapsed times. |
| Databáze: |
Supplemental Index |
| Externí odkaz: |
|