Cui, Tong, Guan, Ren Guo, Qin, Hai Ming, Song, Fu Lin |
| Zdroj: |
Advanced Materials Research; March 2015, Vol. 1095 Issue: 1 p309-313, 5p |
| Abstrakt: |
In vitro degradation behaviour and biological properties of Mg-4.0Zn-2.0Sr alloy sheet had been studied. The results indicate that a novel biodegradable Mg-4.0Zn-2.0Sr (wt. %) alloy sheet was successfully produced using a series of metallurgical processes. The corrosion of Mg-4.0Zn-2.0Sr (wt. %) alloy sheet immersed in SBF occurred as a cyclic process: pitting corrosion →extending of pitting corrosion along grain boundary→ localized corrosion → pitting corrosion again at the new exposed surfaces and the corrosion products were found that contain HA, CaCO3 and MgOH. The change of corrosion rate of Mg-4.0Zn-2.0Sr alloy sheets immersed in SBF is unstable until the 17th day and the average corrosion rate of the alloy sheets was 1.244 g/(m2 • h) after 17 days immersing, which is slightly higher than that of Mg-4.0Zn-1.0Sr alloy sheet 1.163 g/(m2 • h). The corrosion resistance property in SBF of Mg-4.0Zn-2.0Sr alloy is slightly lower than that of Mg-4.0Zn-1.0Sr alloy, which is proved by electrochemical measurements. |
| Databáze: |
Supplemental Index |
| Externí odkaz: |
|