Autor: |
Wang, Xi Jing, Wang, Xiao Long, Zhang, Zhong Ke, Jing, Wen Xia |
Zdroj: |
Applied Mechanics and Materials; September 2014, Vol. 633 Issue: 1 p601-606, 6p |
Abstrakt: |
The 2 mm sheet of 6082 - T6 aluminum alloy was carried to develop refill friction stir welding and withdrawing friction stir spot welding,the forming of solder joints , the cross-sectional microstructure and fracture morphology of welding joints were observed and analyzed, the cross-sectional microhardness of welding joints were tested. Tensile shear load and fracture mode were contrasted simultaneously. The results showed that smooth surface and free of macroscopic defects of welding joints could be obtained in both welding type. Tensile shear load of WFSSW was up to 10.28kN under the optimal process parameters greater than RFSSW’s 8.62kN. |