| Autor: |
Fadzil, Nur Amanina Mohd, Kalam, Anizah, Jumahat, Aidah, Taib, Yakub Md., Razak, Noorrul Wahida Abdul |
| Zdroj: |
Advanced Materials Research; December 2013, Vol. 871 Issue: 1 p184-188, 5p |
| Abstrakt: |
Two different clay loadings were added to OPEFB/PP/MAPP which was 7 phr and 10 phr in order to see its effect on the fracture toughness. Standard dimension of samples was prepared for 180 μm, 355 μm and 355 μm treated with 1% NaOH. The result showed that 7 phr clay contents had the highest fracture toughness of 1.16 MPa.m1/2. Alkali treatment on OPEFB fiber gave 7% improvement of fracture toughness for samples with 7 phr PPnanoclay loading. SEM images show the improvement of bonding between the fibers and the matrix upon alkali treatment. |
| Databáze: |
Supplemental Index |
| Externí odkaz: |
|